ASME SA-106/SA-106M-2015 Carbon steel pipe

Seamless carbon steel tube for high temperature
Request a Quote

PRODUCTS DETAILS

Overview Application Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature,It is widely used in petroleum, chemical industry, boiler, power station, ship, machinery manufacturing, automobile, aviation, aerospace, energy, geology, construction and military industry and other industries. 搜索 复制 Main Grade Grade of high-quality carbon structural steel: GR.A,GR.B,GR.C Chemical Component   Composition, % Grade A Grade B Grade C Carbon, max 0.25A 0.3B 0.35B Manganese 0.27-0.93 0.29-1.06 0.29-1.06 Phosphorus, max 0.035 0.035 0.035 Sulfur, max 0.035 0.035 0.035 Silicon, min 0.10 0.10 0.10 Chrome, maxC 0.40 0.40 0.40 Copper, maxC 0.40 0.40 0.40 Molybdenum, maxC 0.15 0.15 0.15 Nickel, maxC 0.40 0.40 0.40 Vanadium, maxC 0.08 0.08 0.08 A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%. B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%. C These five elements combined shall not exceed 1%. Mechanical Property Grade A Grade B Grade C Tensile strength, min, psi(MPa) 48 000(330) 60 000(415) 70 000(485) Yield strength, min, psi(MPa) 30 000(205) 35 000(240) 40 000(275) Longitudinal Transverse Longitudinal Transverse Longitudinal Transverse Elongation in 2 in. (50 mm), min, % Basic minimum elongation transverse strip tests, and for all small sizes tested in full section 35 25 30 16.5 30 16.5 When standard round 2-in. (50-mm) gauge length test specimen is used 28 20 22 12 20 12 For longitudinal strip tests A A A For transverse strip tests, a deduction for each 1/32-in. (0.8-mm) decrease in wall thickness below 5/16 in. (7.9 mm) from the basic minimum elongation of the following percentage shall be made 1.25 1.00 1.00 A The minimum elongation in 2 in. (50 mm) shall be determined by the following equation: e=625000A 0.2 / U 0.9 for inch-pound units, and e=1940A 0.2 / U 0.9 for SI units, where: e = minimum elongation in 2 in. (50 mm), %, rounded to the nearest 0.5%, A = cross-sectional area of the tension test specimen, in.2 (mm2), based upon specified outside diameter or nominal specified outside diameter or nominal specimen width and specified wall thickness, rounded to the nearest 0.01 in.2 (1 mm2). (If the area thus calculated is equal to or greater than 0.75 in.2 (500 mm2), then the value 0.75 in.2 (500 mm2) shall be used.), and U = specified tensile strength, psi (MPa). Test Requirement In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe. Supply Ability Supply Ability: 1000 Tons Per Month Per Grade of ASTM SA-106 Steel Pipe Packaging In Bundles And In Strong Wooden Box Delivery 7-14 days if in stock, 30-45 days to produce Payment 30% depsoit, 70% L/C or B/L copy   or  100% L/C at sight Product Detail Boiler Tube GB/T5310-2017 ASME SA-106/SA-106M-2015 ASTMA210(A210M)-2012 ASME SA-213/SA-213M ASTM A335/A335M-2018

Contact us

Please feel free to give your inquiry in the form below We will reply you in 24 hours

Leave YourMessage

Thank you! We will reply you via email within 24 hours.

return