2019 China New Design Alloy Pipe Boiler - Seamless Alloy Steel Boiler Pipes Superheater alloy pipes Heat Exchanger Tubes – Sanonpipe

Overview

Application

It is mainly used to make high-quality alloy steel pipe for high pressure boiler pipe, heat exchanger pipe and super heat pipe

Main Grade

Grade of high-quality Alloy steel: T2,T12,T11,T22, T91, T92 etc.

Chemical Component

Steel Grade Chemical Composition%
C Si Mn P, S Max Cr Mo Ni Max V Al Max W B
T2 0.10~0.20 0.10~0.30 0.30~0.61 0.025 0.50~0.81 0.44~0.65
T11 0.05~0.15 0.50~1.00 0.30~0.60 0.025 1.00~1.50 0.44~0.65
T12 0.05~0.15 Max 0.5 0.30~0.61 0.025 0.80~1.25 0.44~0.65
T22 0.05~0.15 Max 0.5 0.30~0.60 0.025 1.90~2.60 0.87~1.13
T91 0.07~0.14 0.20~0.50 0.30~0.60 0.02 8.0~9.5 0.85~1.05 0.4 0.18~0.25 0.015
T92 0.07~0.13 Max 0.5 0.30~0.60 0.02 8.5~9.5 0.30~0.60 0.4 0.15~0.25 0.015 1.50~2.00 0.001~0.006

For T91 other than above also includes Nickel 0.4, Va 0.18-0.25, Ni 0.06-0.10, Ni 0.03-0.07, Al 0.02, Ti 0.01, Zr 0.01. A Maximum, unless range or minimum is indicated. Where ellipses (...) appear in this table, there is no requirement, and analysis for the element need not be determined or reported. B It is permissible to order T2 and T12 with a sulfur content of 0.045 max. C Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.

Mechanical Property

Steel Grade Mechanical Properties
T. S Y. P Elongation Hardness
T2 ≥ 415MPa ≥ 205MPa ≥ 30% 163HBW(85HRB)
T11 ≥ 415MPa ≥ 205MPa ≥ 30% 163HBW(85HRB)
T12 ≥ 415MPa ≥ 220MPa ≥ 30% 163HBW(85HRB)
T22 ≥ 415MPa ≥ 205MPa ≥ 30% 163HBW(85HRB)
T91 ≥ 585MPa ≥ 415MPa ≥ 20% 250HBW(25HRB)
T92 ≥ 620MPa ≥ 440MPa ≥ 20% 250HBW(25HRB)

Tolerance

Permitted Variations in  Wall thickness

Wallthickess %
outside
diameter
in.
mm
0.095
2.4
and under
over0.095
to 0.15
2.4-3.8
incl.
over 0.15
to 0.18
3.8-4.6
incl
over 0.18
to 4.6
                                          over under over under over under over under
seamless, hot finished
4inch and under                   40   0     35    0     33    0    28   0
over 4 inch     ..     ..            35    0     33    0    28   0
seamless, cold finished
over  under
11/2 and under 20     0
over 11/2 22     0

The permitted variations in wall thickness apply only to tube , except internal-upset tubes, as rolled or cold finished

and before swaging,expanding ,bending,polishing,or other fabricating operations

Permitted Variations in  Outside Diameter

outside diameter (mm) Pemitted Variation( mm)
hot finished seamless tube over under
4" (100mm)and under 0.4 0.8
4-71/2"(100-200mm) 0.4 1.2
71/2-9“(200-225) 0.4 1.6
Welded tubes and cold finished seamless tubes
under1"(25mm) 0.1 0.11
1-11/2"(25-40mm) 0.15 0.15
11/2-2"(40-50mm) 0.2 0.2
2-21/2"(50-65mm) 0.25 0.25
21/2-3"(65-75mm) 0.3 0.3
3-4"(75-100mm) 0.38 0.38
4-71/2"(100-200mm) 0.38 0.64
71/2-9“(200-225) 0.38 1.14

Test Requirement

Hydraustatic Test:

The Steel Pipe Should Be Tested Hydraulically One By One. The Maximum Test Pressure Is 20 MPa. Under The Test Pressure, The Stabilization Time Should Be Not Less Than 10 S, And The Steel Pipe Should Not Leak. Or The Hydraulic Test Can Be Replaced By Eddy Current Testing Or Magnetic Flux Leakage Testing.

Nondestructive Test:

Pipes That Require More Inspection Should Be Ultrasonically Inspected One By One. After The Negotiation Requires The Consent Of The Party And Is Specified In The Contract, Other Non-Destructive Testing Can Be Added.

Flattening Test:

Tubes With An Outer Diameter Greater Than 22 Mm Shall Be Subjected To A Flattening Test. No Visible Delamination, White Spots, Or Impurities Should Occur During The Entire Experiment.

Hardness Test:

For Pipe Of Grades P91, P92, P122, And P911, Brinell, Vickers, Or Rockwell Hardness Tests Shall Be Made On A Specimen From Each Lot

 

Product Detail

Boiler Tube

GB/T5310-2017

ASME SA-106/SA-106M-2015

ASTMA210(A210M)-2012

ASME SA-213/SA-213M

ASTM A335/A335M-2018