grade |
Deoxygenated Type a |
% Mass, maximum |
|||||||
|
Steel name |
Steel nmber |
C Prescribed wall thickness mm |
Si |
Mn |
P |
S |
Nbc |
||
|
≤ 40 |
＞ 40≤ 120 |
||||||||
|
S235JRH |
1.0039 |
FN |
0.17 |
0.20 |
— |
1.40 |
0.040 |
0.040 |
0.009 |
|
S275J0H |
1.0149 |
FN |
0.20 |
0.22 |
— |
1.50 |
0.035 |
0.035 |
0.009 |
|
S275J2H |
1.0138 |
FF |
0.20 |
0.22 |
— |
1.50 |
0.030 |
0.030 |
— |
|
S355J0H |
1.0547 |
FN |
0.22 |
0.22 |
0.55 |
1.60 |
0.035 |
0.035 |
0.009 |
|
S355J2H |
1.0576 |
FF |
0.22 |
0.22 |
0.55 |
1.60 |
0.030 |
0.030 |
— |
|
S355K2H |
1.0512 |
FF |
0.22 |
0.22 |
0.55 |
1.60 |
0.030 |
0.030 |
— |
|
a The definition of deoxidation method is as follows: FN = Boiling steel is not allowed FF = fully-killed steel containing nitrogen-binding elements in an amount sufficient to bind possible nitrogen (E.g. 0.020% minimum total aluminum or 0.015% soluble aluminum) b It is allowed to exceed the specified value, as long as the N content increases by 0.001%, the maximum content of P decreases by 0.005% at the same time. The N content in the smelting analysis should not exceed 0.012%. c If the chemical composition shows a minimum total aluminum content of 0.020% and a minimum Al / N ratio of 2: 1, or if other sufficient nitrogen-binding elements are present, the above maximum nitrogen content limits do not apply. Nitrogen binding elements shall be noted in the inspection documents. |
|||||||||
| Grade | Minimum yield | tensile strength | Minimum elongation | Minimum impact power | |||||||||||||
| Steel name | Steel number | Standard thickness | Standard thickness | Standard thickness | Standard thickness | ||||||||||||
| ≤16 | ＞ 16 | ＞ 40 | ＞ 63 | ＞ 80 | ＞ 100 | ≤3 | ＞ 3 | ＞ 100 | ≤40 | ＞40≤63 | ＞63≤100 | ＞100≤120 | -20℃ | 0℃ | 20℃ | ||
| ≤ 40 | ≤ 63 | ≤ 80 | ≤ 100 | ≤ 120 | ≤100 | ≤ 120 | |||||||||||
| S235JRH | 1.0039 | 235 | 225 | 215 | 215 | 215 | 195 | 360-510 | 360-510 | 360-500 | 26 | 25 | 24 | 22 | - | - | 27 |
| S275J0Hc | 1.0149 | 275 | 265 | 255 | 245 | 235 | 225 | 430-580 | 410-560 | 400-540 | 23 | 22 | 21 | 19 | - | 27 | - |
| S275J2H | 1.0138 | 27 | - | - | |||||||||||||
| S355J0Hc | 1.0547 | 355 | 345 | 355 | 325 | 315 | 295 | 510-680 | 470-630 | 450-600 | 22 | 21 | 20 | 18 | - | 27 | - |
| S355J2H | 1.0576 | 27 | - | - | |||||||||||||
| S355K2H | 1.0512 | 40 | - | - | |||||||||||||
| a Longitudinal sample value. The standard value of the transverse specimen is 2% lower than this value.b For thicknesses <3mm, see 9.2.2.c Only when option 1.3 is applied, confirmation of impact performance is required.d See 6.6.2 for the impact properties of small-sized specimens.e This value is equivalent to 27J at -30 ° C (see EN 1993-1-1). | |||||||||||||||||