Hot Sale for Seamless Tube A333 T9 - Hot finished structural hollow sections of non-alloy and fine grain steels – Sanonpipe

Overview

Application

It Is Mainly Used for Mechanical structure,general structure.

Main Grade

S235GRH, S275JOH, S275J2H, S355JOH, S355J2H

Chemical Component

grade

Deoxygenated

Type a

% Mass, maximum

Steel name

Steel nmber

C

Prescribed wall thickness  mm

Si

Mn

P

S

Nbc

≤ 40

> 40≤ 120

S235JRH

1.0039

FN

0.17

0.20

1.40

0.040

0.040

0.009

S275J0H

1.0149

FN

0.20

0.22

1.50

0.035

0.035

0.009

S275J2H

1.0138

FF

0.20

0.22

1.50

0.030

0.030

S355J0H

1.0547

FN

0.22

0.22

0.55

1.60

0.035

0.035

0.009

S355J2H

1.0576

FF

0.22

0.22

0.55

1.60

0.030

0.030

S355K2H

1.0512

FF

0.22

0.22

0.55

1.60

0.030

0.030

a The definition of deoxidation method is as follows:

FN = Boiling steel is not allowed

FF = fully-killed steel containing nitrogen-binding elements in an amount sufficient to bind possible nitrogen

(E.g. 0.020% minimum total aluminum or 0.015% soluble aluminum)

b It is allowed to exceed the specified value, as long as the N content increases by 0.001%, the maximum content of P decreases by 0.005% at the same time. The N content in the smelting analysis should not exceed 0.012%.

c If the chemical composition shows a minimum total aluminum content of 0.020% and a minimum Al / N ratio of 2: 1, or if other sufficient nitrogen-binding elements are present, the above maximum nitrogen content limits do not apply. Nitrogen binding elements shall be noted in the inspection documents.

Mechanical Property

Grade

Minimum yield tensile strength Minimum elongation Minimum impact power

Steel name

Steel number

Standard thickness Standard thickness Standard thickness Standard thickness

≤16

 

> 16

≤ 40

> 40

≤ 63

> 63

≤ 80 

> 80

≤ 100

> 100

≤ 120

≤3

> 3

100

> 100

≤ 120 

≤40

>40≤63 >63≤100 >100≤120 -20 0 20
S235JRH 1.0039 235 225 215 215 215 195 360-510 360-510 360-500 26 25 24 22 - - 27
S275J0Hc 1.0149 275 265 255 245 235 225 430-580 410-560 400-540 23 22 21 19 - 27 -
S275J2H 1.0138 27 - -
S355J0Hc 1.0547 355 345 355 325 315 295 510-680 470-630 450-600 22 21 20 18 - 27 -
S355J2H 1.0576 27 - -
S355K2H 1.0512 40 - -
a Longitudinal sample value. The standard value of the transverse specimen is 2% lower than this value.b For thicknesses <3mm, see 9.2.2.c Only when option 1.3 is applied, confirmation of impact performance is required.d See 6.6.2 for the impact properties of small-sized specimens.e This value is equivalent to 27J at -30 ° C (see EN 1993-1-1).

Test Requirement

Hardness Test, Tension Tests, Nondestructive Tests, Steel Cleanliness, Hardenability, Flaring Test

Supply Ability

Supply Ability: 2000 Tons Per Month Per Grade Of BSEN10210-1-2006 Steel Pipe

Packaging

In Bundles And In Strong Wooden Box

Delivery

7-14 days if in stock, 30-45 days to produce

Payment

30% depsoit, 70% L/C or B/L copy   or  100% L/C at sight

Product Detail

Seamless Steel Tubes For Mechanical Engineering And Normal Structure

GB/T8162-2008

ASTM A519-2006

BS EN 10210-1-2006

ASTM A53/A53M-2012

GB9948-2006

GB6479-2013

GB/T 17396-2009