It adheres on the tenet "Honest, industrious, enterprising, innovative" to acquire new solutions continuously. It regards prospects, success as its personal success. Let us build prosperous future hand in hand for Seamless Carbon Steel Fluid Pipe, We now have developed a responsible name amongst many customers. Quality&customer very first are usually our constant pursuit. We spare no endeavours to help make much better solutions. Look forward to long-term cooperation and mutual advantages! So far our merchandise have been exported to east Europe, the Middle East, Southeast, Africa and South America etc. We've 13years expert sales and purchase in Isuzu parts at home and abroad and the ownership of the modernized electronic Isuzu parts checking systems. We honor our core principal of Honesty in business, priority in service and will do our best to provide our customers with high quality goods and excellent service.
Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature
Grade of high-quality carbon structural steel: GR.A,GR.B,GR.C
Composition, % | |||
Grade A | Grade B | Grade C | |
Carbon, max | 0.25A | 0.3B | 0.35B |
Manganese | 0.27-0.93 | 0.29-1.06 | 0.29-1.06 |
Phosphorus, max | 0.035 | 0.035 | 0.035 |
Sulfur, max | 0.035 | 0.035 | 0.035 |
Silicon, min | 0.10 | 0.10 | 0.10 |
Chrome, maxC | 0.40 | 0.40 | 0.40 |
Copper, maxC | 0.40 | 0.40 | 0.40 |
Molybdenum, maxC | 0.15 | 0.15 | 0.15 |
Nickel, maxC | 0.40 | 0.40 | 0.40 |
Vanadium, maxC | 0.08 | 0.08 | 0.08 |
A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%. | |||
B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%. | |||
C These five elements combined shall not exceed 1%. |
Grade A | Grade B | Grade C | ||||||
Tensile strength, min, psi(MPa) | 48 000(330) | 60 000(415) | 70 000(485) | |||||
Yield strength, min, psi(MPa) | 30 000(205) | 35 000(240) | 40 000(275) | |||||
Longitudinal | Transverse | Longitudinal | Transverse | Longitudinal | Transverse | |||
Elongation in 2 in. (50 mm), min, % Basic minimum elongation transverse strip tests, and for all small sizes tested in full section |
35 | 25 | 30 | 16.5 | 30 | 16.5 | ||
When standard round 2-in. (50-mm) gauge length test specimen is used | 28 | 20 | 22 | 12 | 20 | 12 | ||
For longitudinal strip tests | A | A | A | |||||
For transverse strip tests, a deduction for each 1/32-in. (0.8-mm) decrease in wall thickness below 5/16 in. (7.9 mm) from the basic minimum elongation of the following percentage shall be made | 1.25 | 1.00 | 1.00 | |||||
A The minimum elongation in 2 in. (50 mm) shall be determined by the following equation: | ||||||||
e=625000A 0.2 / U 0.9 | ||||||||
for inch-pound units, and | ||||||||
e=1940A 0.2 / U 0.9 | ||||||||
for SI units, | ||||||||
where: e = minimum elongation in 2 in. (50 mm), %, rounded to the nearest 0.5%, A = cross-sectional area of the tension test specimen, in.2 (mm2), based upon specified outside diameter or nominal specified outside diameter or nominal specimen width and specified wall thickness, rounded to the nearest 0.01 in.2 (1 mm2). (If the area thus calculated is equal to or greater than 0.75 in.2 (500 mm2), then the value 0.75 in.2 (500 mm2) shall be used.), and U = specified tensile strength, psi (MPa). |
In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe.
Supply Ability: 1000 Tons Per Month Per Grade of ASTM SA-106 Steel Pipe
In Bundles And In Strong Wooden Box
7-14 days if in stock, 30-45 days to produce
30% depsoit, 70% L/C or B/L copy or 100% L/C at sight