We pursue the administration tenet of "Quality is top-quality, Company is supreme, Track record is first", and will sincerely create and share success with all purchasers for Seamless Steel Pipe. Our products are widely recognized and trusted by users and can meet continuously developing economic and social needs. Our factory covers an area of 12,000 square meters, and has a staff of 200 people, among which there are 5 technical executives. We have been specialized in producing.We now have rich experience in export. Welcome to contact us and your enquiry will probably be replied as soon as possible.
Compare with corresponding China Steel Grade GB/T 8163 20#:
Chemical Component(%):
C: 0.07~0.13
Si: 0.17~0.37
Mn: 0.35~0.65
p: <=0.03
S: <=0.03
Cr: 0.15
Ni: 0.3
Cu: 0.2
Mechanical property(Mpa):
Tensile Strength: 410~530
Yield Strength: 245
Elogation(%): 20
Both no required heat treatment and impact test, and A106 Gr.B nearly covered 20# in chemical component and mechanical property, so this two steel grade usually be mutual substitute.
Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature
Grade of high-quality carbon structural steel: GR.A,GR.B,GR.C
Composition, % | |||
Grade A | Grade B | Grade C | |
Carbon, max | 0.25A | 0.3B | 0.35B |
Manganese | 0.27-0.93 | 0.29-1.06 | 0.29-1.06 |
Phosphorus, max | 0.035 | 0.035 | 0.035 |
Sulfur, max | 0.035 | 0.035 | 0.035 |
Silicon, min | 0.10 | 0.10 | 0.10 |
Chrome, maxC | 0.40 | 0.40 | 0.40 |
Copper, maxC | 0.40 | 0.40 | 0.40 |
Molybdenum, maxC | 0.15 | 0.15 | 0.15 |
Nickel, maxC | 0.40 | 0.40 | 0.40 |
Vanadium, maxC | 0.08 | 0.08 | 0.08 |
A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%. | |||
B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%. | |||
C These five elements combined shall not exceed 1%. |
Grade A | Grade B | Grade C | ||||||
Tensile strength, min, psi(MPa) | 48 000(330) | 60 000(415) | 70 000(485) | |||||
Yield strength, min, psi(MPa) | 30 000(205) | 35 000(240) | 40 000(275) | |||||
Longitudinal | Transverse | Longitudinal | Transverse | Longitudinal | Transverse | |||
Elongation in 2 in. (50 mm), min, % Basic minimum elongation transverse strip tests, and for all small sizes tested in full section |
35 | 25 | 30 | 16.5 | 30 | 16.5 | ||
When standard round 2-in. (50-mm) gauge length test specimen is used | 28 | 20 | 22 | 12 | 20 | 12 | ||
For longitudinal strip tests | A | A | A | |||||
For transverse strip tests, a deduction for each 1/32-in. (0.8-mm) decrease in wall thickness below 5/16 in. (7.9 mm) from the basic minimum elongation of the following percentage shall be made | 1.25 | 1.00 | 1.00 | |||||
A The minimum elongation in 2 in. (50 mm) shall be determined by the following equation: | ||||||||
e=625000A 0.2 / U 0.9 | ||||||||
for inch-pound units, and | ||||||||
e=1940A 0.2 / U 0.9 | ||||||||
for SI units, | ||||||||
where: e = minimum elongation in 2 in. (50 mm), %, rounded to the nearest 0.5%, A = cross-sectional area of the tension test specimen, in.2 (mm2), based upon specified outside diameter or nominal specified outside diameter or nominal specimen width and specified wall thickness, rounded to the nearest 0.01 in.2 (1 mm2). (If the area thus calculated is equal to or greater than 0.75 in.2 (500 mm2), then the value 0.75 in.2 (500 mm2) shall be used.), and U = specified tensile strength, psi (MPa). |
In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe.
Supply Ability: 1000 Tons Per Month Per Grade of ASTM SA-106 Steel Pipe
In Bundles And In Strong Wooden Box
7-14 days if in stock, 30-45 days to produce
30% depsoit, 70% L/C or B/L copy or 100% L/C at sight