China Hot Dipped Seamless Steel Pipe/Welded Steel Pipe, ASTM A53 API 5L

Overview

It can be our accountability to satisfy your preferences and competently provide you. Your satisfaction is our greatest reward. We are seeking ahead towards your visit for joint growth. Because of our efforts, our goods have won the trust of buyers and been very salable equally here and abroad. Our factory insists on the principle of "Quality First, Sustainable Development", and takes "Honest Business, Mutual Benefits" as our developable goal. All members sincerely thanks for all old and new customers' support. We will keep working hard and offering you the highest-quality products and service.

About carbon steel welded and seamless pipe, for increase corrossion resistance ability, there will be some kind surface treatment for pipe. One of the mostly be used is zinc coat(galvanize). There is two kind galvanize method: cold glavanizing(electrogalvanizing) and hot galvanizing. Because environment problem, cold glavanizing has been limited in China, and hot galvanizing also can't be used as water supply pipe, but it widely be used in firefighting, electricity and highway.

Cold galvanizing is electrogalvanizing, because of the limit of technique, zinc coat is not much, mainly in 10-50g/m2, therefore, its corrossion resistance ability is less than hot galvanizing. The Ministry of Construction has officially put an end to the elimination of cold galvanized pipes with backward technology, and it is forbidden to use cold galvanized pipes for water and gas pipes. The galvanized layer of the cold-dip galvanized steel pipe is an electroplated layer, and the zinc layer and the steel pipe substrate are layered independently. The zinc layer is relatively thin, and the zinc layer simply adheres to the steel pipe substrate and is easy to fall off. Therefore, its corrosion resistance is poor.

Hot galvanizing pipe's alloy layer is formed by the reaction of the molten metal and the iron substrate, so that the substrate and the plating layer are combined, and the plating layer is not easy to fall off. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life. The hot-dip galvanized steel pipe substrate and the molten plating solution undergo complex physical and chemical reactions to form a corrosion-resistant zinc-iron alloy layer with a compact structure. The alloy layer is integrated with the pure zinc layer and the steel pipe substrate, so its corrosion resistance is strong.

Application

It Is Mainly Used for force and pressure parts, and for general purpose steam, water, gas and air pipes.

Main Grade

GR.A, GR.B

Chemical Component

Grade

 Component %,≤
C Mn P S

    CuA

  NiA

CrA

MoA VA
S type(seamless pipe)
GR.A 0.25B 0.95 0.05 0.045

0.40

0.40

0.40

0.15 0.08
GR.B 0.30C 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08
E type(Resistance welded pipe)
GR.A 0.25B 0.95 0.05 0.045

0.40

0.40

0.40

0.15 0.08
GR.B 0.30C 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08
F type(Furnace Welded Pipe)
A 0.30B 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08

A The sum of these five elements must not be greater than 1.00%。

B For every 0.01% decrease in the maximum carbon content, the maximum manganese content is allowed to increase by 0.06%, but the maximum cannot exceed 1.35%.

C Each 0.01% decrease in the maximum carbon content will allow the maximum manganese content to increase by 0.06%, but the maximum must not exceed 1.65%.

Mechanical Property

item GR.A GR.B

tensile strength, ≥, psi [MPa]

Yield Strength, ≥, psi [MPa]

Gauge 2in.or 50mm elongation

48 000 [330]30 000 [205]A,B 60 000 [415]35 000 [240]A,B

A The minimum elongation of gauge length 2in. (50mm) shall be determined by the following formula:

e=625000(1940)A0.2/U0.9

e = the minimum elongation of the gauge 2in. (50mm), the percentage rounded to the nearest 0.5%;

A = Calculated according to the specified outer diameter of the nominal tube or the nominal width of the tensile sample and its specified wall thickness, and rounded to the nearest cross-sectional area of the tensile sample of 0.01 in.2 (1 mm2), and It is compared with 0.75in.2 (500mm2), whichever is smaller.

U = specified minimum tensile strength, psi (MPa).

B For various combinations of different sizes of tensile test specimens and prescribed minimum tensile strength, the required minimum elongation is shown in Table X4.1 or Table X4.2, according to its applicability.

Test Requirement

Tensile test, bending test, hydrostatic test, nondestructive electrical test of welds.

Supply Ability

Supply Ability: 2000 Tons Per Month Per Grade Of ASTM A53/A53M-2012 Steel Pipe

Packaging

In Bundles And In Strong Wooden Box

Delivery

7-14 days if in stock, 30-45 days to produce

Payment

30% depsoit, 70% L/C or B/L copy   or  100% L/C at sight

Product Detail

Boiler Tube


GB/T 8162-2008


ASTM A519-2006


BS EN10210-1-2006


ASTM A53/A53M-2012


GB9948-2006


GB6479-2013


GB/T 17396-2009