We believe that prolonged expression partnership is really a result of top of the range, value added support, rich encounter and personal contact for Carbon Steel Pipe, We also make sure that your assortment will be crafted while using the optimum quality and dependability. Make sure you experience totally free to make contact with us for more information and facts. We're introduced as a one of the growing manufacture supplier and export of carbon steel and alloy steel pipe. Now we have a team of dedicated trained experienced who take care the quality and timely supply. If you are looking for Good Quality at a good price and timely delivery. Do contact us.
A106 seamless steel pipe is a seamless steel pipe used to transport high-temperature fluids such as water, oil, and gas. This steel grade has high cold deformation and high plasticity, cold drawn or normalized state is better than annealed state, generally used for fluid pipes, structural pipes, low pressure boiler pipes that are not stressed and require high toughness
Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature
Grade of high-quality carbon structural steel: GR.A,GR.B,GR.C
| Composition, ％ | |||
| Grade A | Grade B | Grade C | |
| Carbon, max | 0.25A | 0.3B | 0.35B |
| Manganese | 0.27-0.93 | 0.29-1.06 | 0.29-1.06 |
| Phosphorus, max | 0.035 | 0.035 | 0.035 |
| Sulfur, max | 0.035 | 0.035 | 0.035 |
| Silicon, min | 0.10 | 0.10 | 0.10 |
| Chrome, maxC | 0.40 | 0.40 | 0.40 |
| Copper, maxC | 0.40 | 0.40 | 0.40 |
| Molybdenum, maxC | 0.15 | 0.15 | 0.15 |
| Nickel, maxC | 0.40 | 0.40 | 0.40 |
| Vanadium, maxC | 0.08 | 0.08 | 0.08 |
| A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%. | |||
| B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%. | |||
| C These five elements combined shall not exceed 1%. | |||
| Grade A | Grade B | Grade C | ||||||
| Tensile strength, min, psi(MPa) | 48 000(330) | 60 000(415) | 70 000(485) | |||||
| Yield strength, min, psi(MPa) | 30 000(205) | 35 000(240) | 40 000(275) | |||||
| Longitudinal | Transverse | Longitudinal | Transverse | Longitudinal | Transverse | |||
| Elongation in 2 in. (50 mm), min, % Basic minimum elongation transverse strip tests, and for all small sizes tested in full section |
35 | 25 | 30 | 16.5 | 30 | 16.5 | ||
| When standard round 2-in. (50-mm) gauge length test specimen is used | 28 | 20 | 22 | 12 | 20 | 12 | ||
| For longitudinal strip tests | A | A | A | |||||
| For transverse strip tests, a deduction for each 1/32-in. (0.8-mm) decrease in wall thickness below 5/16 in. (7.9 mm) from the basic minimum elongation of the following percentage shall be made | 1.25 | 1.00 | 1.00 | |||||
| A The minimum elongation in 2 in. (50 mm) shall be determined by the following equation: | ||||||||
| e=625000A 0.2 / U 0.9 | ||||||||
| for inch-pound units, and | ||||||||
| e=1940A 0.2 / U 0.9 | ||||||||
| for SI units, | ||||||||
| where: e = minimum elongation in 2 in. (50 mm), %, rounded to the nearest 0.5%, A = cross-sectional area of the tension test specimen, in.2 (mm2), based upon specified outside diameter or nominal specified outside diameter or nominal specimen width and specified wall thickness, rounded to the nearest 0.01 in.2 (1 mm2). (If the area thus calculated is equal to or greater than 0.75 in.2 (500 mm2), then the value 0.75 in.2 (500 mm2) shall be used.), and U = specified tensile strength, psi (MPa). |
||||||||
In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe.
Supply Ability: 1000 Tons Per Month Per Grade of ASTM SA-106 Steel Pipe
In Bundles And In Strong Wooden Box
7-14 days if in stock, 30-45 days to produce
30% depsoit, 70% L/C or B/L copy or 100% L/C at sight