Api5ct Oil Casing Is Mainly Used To Transport Oil, Natural Gas, Gas, Water And Other Liquids And Gases
Grade :J55,K55,N80,L80,P110, etc
|
Grade |
Type |
Total Elongation Under Load |
Yield Strength |
Tensile Strength |
Hardness a,c |
Specified Wall Thickness |
Allowable Hardness Variation b |
||
|
|
|
|
|
|
|
|
||
|
|
|
min |
max |
|
HRC |
HBW |
mm |
HRC |
H40 |
— |
0.5 |
276 |
552 |
414 |
— |
— |
— |
— |
J55 |
— |
0.5 |
379 |
552 |
517 |
— |
— |
— |
— |
K55 |
— |
0.5 |
379 |
552 |
655 |
— |
— |
— |
— |
N80 |
1 |
0.5 |
552 |
758 |
689 |
— |
— |
— |
— |
N80 |
Q |
0.5 |
552 |
758 |
689 |
— |
— |
— |
— |
R95 |
— |
0.5 |
655 |
758 |
724 |
— |
— |
— |
— |
L80 |
1 |
0.5 |
552 |
655 |
655 |
23.0 |
241.0 |
— |
— |
L80 |
9Cr |
0.5 |
552 |
655 |
655 |
23.0 |
241.0 |
— |
— |
L80 |
l3Cr |
0.5 |
552 |
655 |
655 |
23.0 |
241.0 |
— |
— |
C90 |
1 |
0.5 |
621 |
724 |
689 |
25.4 |
255.0 |
≤12.70 |
3.0 |
12.71 to 19.04 |
4.0 |
||||||||
19.05 to 25.39 |
5.0 |
||||||||
≥25.4 |
6.0 |
||||||||
T95 |
1 |
0.5 |
655 |
758 |
724 |
25.4 |
255 |
≤12.70 |
3.0 |
12.71 to 19.04 |
4.0 |
||||||||
19.05 to 25.39 |
5.0 |
||||||||
≥25.4 |
6.0 |
||||||||
C110 |
— |
0.7 |
758 |
828 |
793 |
30.0 |
286.0 |
≤12.70 |
3.0 |
12.71 to 19.04 |
4.0 |
||||||||
19.05 to 25.39 |
5.0 |
||||||||
≥25.4 |
6.0 |
||||||||
P110 |
— |
0.6 |
758 |
965 |
862 |
— |
— |
— |
— |
Q125 |
1 |
0.65 |
862 |
1034 |
931 |
b |
— |
≤12.70 |
3.0 |
12.71 to 19.04 |
4.0 |
||||||||
19.05 |
5.0 |
||||||||
a In case of dispute, laboratory Rockwell C hardness testing shall be used as the referee method. | |||||||||
b No hardness limits are specified, but the maximum variation is restricted as a manufacturing control in accordance with 7.8 and 7.9. | |||||||||
c For through-wall hardness tests of Grades L80 (all types), C90, T95 and C110, the requirements stated in HRC scale are for maximum mean hardness number. |
In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe.
Supply Ability: 500 Tons Per Month Per Grade of API 5CT PIPE
In Bundles And In Strong Wooden Box
7-14 days if in stock, 30-45 days to produce
30% depsoit, 70% L/C or B/L copy or 100% L/C at sight