To meet the customers' over-expected pleasure , we've our sturdy group to offer our best overall service which incorporates advertising and marketing, product sales, designing, production, good quality managing, packing, warehousing and logistics for Seamless Welded Steel Tube / Carbon Mild Low Alloy Steel Pipe, Our intention is "blazing new floor, Passing Value", in the upcoming, we sincerely invite you to definitely improve up with us and make a shiny long term together! Our company has built stable business relationships with many well-known domestic companies as well as oversea customers. With the goal of providing high quality products and solutions to customers at low cots, we've been committed to improving its capacities in research, development, manufacturing and management. We've honored to receive recognition from our customers. Till now we've got passed ISO9001in 2005 and ISO/TS16949 in 2008. Enterprises of "quality of survival, the credibility of development" for the purpose, sincerely welcome domestic and foreign businessmen to visit to discuss cooperation.
ASTM A672 is a common high-voltage electrofusion welded pipe standard. The temperature range of the materials listed in the standard is from 20°C to -195°C. Therefore, the A672 standard is often used for low-temperature welded pipes. Among them, CC60 CL22 is a commonly used low-temperature pipe material, which is made of A516GR.60 medium and low-temperature pressure vessel carbon steel plates. It is an important material for electric welded pipes. The impact test temperature is required to be -50°C, which can be replaced by Chinese material Q345R. The chemical composition and mechanical properties of the two are similar:
CC60:
C: 0.23%; Mn: 0.55%~1.3%; Si: 0.13%~0.45%; P: 0.025% S: 0.025
Tensile strength: 415~550Mpa
Yield strength: 220Mpa
Elongation: 21%
Q345R:
C: 0.22%; Mn: 1.6%; Si: 0.55%; P: 0.025% S: 0.025
Tensile strength: 470~630Mpa
Yield strength: 345Mpa
Elongation: 21%
It Is Mainly Used To Make Carbon Structural Steel, Alloy Structural Steel and mechanical structures.
Grade Of Carbon Structural Steel: 10,20,35, 45,Q345,Q460,Q490,Q620,, Etc
Grade Of Alloy Structural Steel: 42CrMo,35CrMo, Etc
Steel Grade |
Quality level |
Chemical composition |
||||||||||||||
C |
Si |
Mn |
P |
S |
Nb |
V |
Ti |
Cr |
Ni |
Cu |
Nd |
Mo |
B |
Als" |
||
no greater than |
not less than |
|||||||||||||||
Q345 | A |
0.20 |
0.50 |
1.70 |
0.035 | 0.035 |
0.30 |
0.50 |
0.20 |
0.012 |
0.10 |
—— | — | |||
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 |
0.07 |
0.15 |
0.20 |
0.015 |
||||||||||
D |
0.18 |
0.030 | 0.025 | |||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q390 | A |
0.20 |
0.50 |
1.70 |
0.035 | 0.035 |
0.07 |
0.20 |
0.20 |
0.3 |
0.50 |
0.20 |
0.015 |
0.10 |
— | — |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 |
0,015 |
|||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q42O | A |
0.20 |
0.50 |
1.70 |
0.035 | 0.035 |
0.07 |
0.2 |
0.20 |
0.30 |
0.80 |
0.20 |
0.015 |
0.20 |
—— |
—— |
B | 0.035 | 0.035 | ||||||||||||||
C | 0.030 | 0.030 |
0.015 |
|||||||||||||
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q46O | C |
0.20 |
0.60 |
1.80 |
0.030 | 0.030 |
0.11 |
0.20 |
0.20 |
0.30 |
0.80 |
0.20 |
0.015 |
0.20 |
0.005 |
0.015 |
D | 0.030 | 0.025 | ||||||||||||||
E | 0.025 | 0.020 | ||||||||||||||
Q500 | C |
0J8 |
0.60 |
1.80 |
0.025 | 0.020 |
0.11 |
0.20 |
0.20 |
0.60 |
0.80 |
0.20 |
0.015 |
0.20 |
0.005 |
0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q550 | C |
0.18 |
0.60 |
2.00 |
0.025 | 0,020 | 0.11 |
0.20 |
0.20 |
0.80 |
0.80 |
0.20 |
0.015 |
0.30 |
0.005 |
0.015 |
D | 0.025 | 0,015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
Q62O | C |
0.18 |
0.60 |
2.00 |
0.025 | 0.020 |
0.11 |
0.20 |
0.20 |
1.00 |
0.80 |
0.20 |
0.015 |
0.30 |
0.005 |
0.015 |
D | 0.025 | 0.015 | ||||||||||||||
E | 0.020 | 0.010 | ||||||||||||||
a. In addition to Q345A and Q345B grades, the steel should contain at least one of the refined grain elements Al, Nb, V, and Ti. According to the needs, the supplier can add one or more refined grain elements. The maximum value shall be as specified in the table. When combined, Nb + V + Ti is not more than 0.22%b. For Q345, Q390, Q420 and Q46O grades, Mo + Cr is not greater than 0.30%c. When Cr and Ni of each grade are used as residual elements, the content of Cr and Ni should not be greater than 0.30%; when it is necessary to add, the content should meet the requirements in the table or be determined by the supplier and the buyer through consultation.d. If the supplier can ensure that the nitrogen content meets the requirements in the table, the nitrogen content analysis may not be performed. If Al, Nb, V, Ti and other alloy elements with nitrogen fixation are added to the steel, the nitrogen content is not limited. The nitrogen fixation content should be specified in the quality certificate.e. When using full aluminum, the total aluminum content Alt ≥ 0020%. |
Grade |
Carbon equivalent CEV (mass fraction) /% |
|||||
Nominal wall thickness s≤ 16mm |
Nominal wall thickness S2>16 mm〜30 mm |
Nominal wall thickness S>30mm |
||||
Hot rolled or normalized normalized |
Quenching +tempering |
Hot rolled or normalized |
Quenching +tempering |
Hot rolled or normalized |
Quenching +tempering |
|
Q345 |
<0.45 |
— |
<0.47 |
— |
<0.48 |
一 |
Q390 |
<0.46 |
一 |
W0.48 |
— |
<0.49 |
— |
Q420 |
<0.48 |
一 |
<0.50 |
<0.48 |
<0.52 |
<0,48 |
Q460 |
<0.53 |
<0.48 |
W0.55 |
<0.50 |
<0.55 |
W0.50 |
Q500 |
一 |
<0.48 |
一 |
<0.50 |
一 |
W0.50 |
Q550 |
— |
<0.48 |
.一 |
<0.50 |
一 |
<0.50 |
Q62O |
— |
<0.50 |
— |
<0.52 |
— |
W0.52 |
Q690 |
— |
<0.50 |
— |
<0.52 |
— |
W0.52 |
Mechanical properties of high-quality carbon steel structural steel and low-alloy high-strength structural steel pipes
Grade | Quality level | Yield Strength | Lower yield strength | Elongation after breaking | Impact test | |||
Nominal wall thickness | temperature | Absorb energy | ||||||
<16 mm | >16 mm〜 | 〉30 mm | ||||||
30 mm | ||||||||
not less than | not less than | |||||||
10 | — | >335 | 205 | 195 | 185 | 24 | — | — |
15 | — | >375 | 225 | 215 | 205 | 22 | — | 一 |
20 | —— | >410 | 245 | 235 | 225 | 20 | — | — |
25 | — | >450 | 275 | 265 | 255 | 18 | — | — |
35 | — | >510 | 305 | 295 | 285 | 17 | 一 | — |
45 | — | 2590 | 335 | 325 | 315 | 14 | — | — |
20Mn | —• | >450 | 275 | 265 | 255 | 20 | — | 一 |
25Mn | — | >490 | 295 | 285 | 275 | 18 | — | — |
Q345 | A | 470—630 | 345 | 325 | 295 | 20 | — | 一 |
B | 4~20 | 34 | ||||||
C | 21 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q39O | A | 490—650 | 390 | 370 | 350 | 18 | ||
B | 20 | 34 | ||||||
C | 19 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q42O | A | 520〜680 | 420 | 400 | 380 | 18 | ||
B | 20 | 34 | ||||||
C | 19 | 0 | ||||||
D | -20 | |||||||
E | -40 | 27 | ||||||
Q46O | C | 550〜720 | 460 | 440 | 420 | 17 | 0 | 34 |
D | -20 | |||||||
E | -40 | 27 | ||||||
Q500 | C | 610〜770 | 500 | 480 | 440 | 17 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q550 | C | 670〜830 | 550 | 530 | 490 | 16 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q62O | C | 710〜880 | 620 | 590 | 550 | 15 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 | ||||||
Q690 | C | 770〜94。 | 690 | 660 | 620 | 14 | 0 | 55 |
D | -20 | 47 | ||||||
E | -40 | 31 |
Mechanical properties of alloy steel pipes
NO | Grade | Recommended heat treatment regime | Tensile properties | Annealed or high temperature tempered steel pipe Delivery condition Brinell hardness HBW | ||||||
Quenching (normalizing) | Tempering | Yield StrengthMPa | Tensile Strength MPa | Elongation after breaking A% | ||||||
temperature | Coolant | Temperature | Coolant | |||||||
Frirst | Second | not less than | no greater than | |||||||
1 | 40Mn2 | 840 | Water, oil | 540 | Water, oil | 885 | 735 | 12 | 217 | |
2 | 45Mn2 | 840 | Water,oil | 550 | Water, oil | 885 | 735 | 10 | 217 | |
3 | 27SiMn | 920 | Water | 450 | Water, oil | 980 | 835 | 12 | 217 | |
4 | 40MnBc | 850 | oil | 500 | Water, oil | 980 | 785 | 10 | 207 | |
5 | 45MnBc | 840 | oil | 500 | Water, oil | 1 030 | 835 | 9 | 217 | |
6 | 20Mn2Bc'f | 880 | oil | 200 | Water, air | 980 | 785 | 10 | 187 | |
7 | 20CrdJ | 880 | 800 | Water,oil | 200 | Water, air | 835 | 540 | 10 | 179 |
785 | 490 | 10 | 179 | |||||||
8 | 30Cr | 860 | oil | 500 | Water, oil | 885 | 685 | 11 | 187 | |
9 | 35Cr | 860 | oil | 500 | Water, oil | 930 | 735 | 11 | 207 | |
10 | 40Cr | 850 | oil | 520 | Water, oil | 980 | 785 | 9 | 207 | |
11 | 45Cr | 840 | oil | 520 | Water, oil | 1 030 | 835 | 9 | 217 | |
12 | 50Cr | 830 | oil | 520 | Water, oil | 1 080 | 930 | 9 | 229 | |
13 | 38CrSi | 900 | oil | 600 | Water, oil | 980 | 835 | 12 | 255 | |
14 | 20CrModJ | 880 | Water,oil | 500 | Water, oil | 885 | 685 | 11 | 197 | |
845 | 635 | 12 | 197 | |||||||
15 | 35CrMo | 850 | oil | 550 | Water, oil | 980 | 835 | 12 | 229 | |
16 | 42CrMo | 850 | oil | 560 | Water, oil | 1 080 | 930 | 12 | 217 | |
17 | 38CrMoAld | 940 | Water, oil | 640 | Water, oil | 980 | 835 | 12 | 229 | |
930 | 785 | 14 | 229 | |||||||
18 | 50CrVA | 860 | oil | 500 | Water, oil | 1 275 | 1 130 | 10 | 255 | |
19 | 2OCrMn | 850 | oil | 200 | Water、air | 930 | 735 | 10 | 187 | |
20 | 20CrMnSif | 880 | oil | 480 | Water, oil | 785 | 635 | 12 | 207 | |
21 | 3OCrMnSif | 880 | oil | 520 | Water, oil | 1 080 | 885 | 8 | 229 | |
980 | 835 | 10 | 229 | |||||||
22 | 35CrMnSiA£ | 880 | oil | 230 | Water、air | 1 620 | 9 | 229 | ||
23 | 20CrMnTie-f | 880 | 870 | oil | 200 | Water、air | 1 080 | 835 | 10 | 217 |
24 | 30CrMnTie*f | 880 | 850 | oil | 200 | Water、air | 1 470 | 9 | 229 | |
25 | 12CrNi2 | 860 | 780 | Water,oil | 200 | Water、air | 785 | 590 | 12 | 207 |
26 | 12CrNi3 | 860 | 780 | oil | 200 | Water、air | 930 | 685 | 11 | 217 |
27 | 12Cr2Ni4 | 860 | 780 | oil | 200 | Water、air | 1 080 | 835 | 10 | 269 |
28 | 40CrNiMoA | 850 | —— | oil | 600 | Water、air | 980 | 835 | 12 | 269 |
29 | 45CrNiMoVA | 860 | — | oil | 460 | oil | 1 470 | 1 325 | 7 | 269 |
a. Allowable adjustment range of heat treatment temperature listed in the table: quenching ± 15 ℃, low temperature tempering ± 20 ℃, high temperature tempering soil 50 ℃.b. In the tensile test, transverse or longitudinal samples can be taken. In case of disagreement, the longitudinal sample is used as the basis for arbitration.c. Boron-containing steel can be normalized before quenching, and the normalizing temperature should not be higher than its quenching temperature.d. Delivery according to a set of data specified by the demander. When the demander has not specified, delivery can be made according to any of the data.
e. The first quenching of titanium steel with Ming Meng can be replaced by normalizing. f. Isothermal quenching at 280 C ~320 C. g. In the tensile test, if Rel cannot be measured, Rp0.2 can be measured instead of Rel. |
Chemical composition:
Stretch,Hardness,Shock,Squash,Bending,Ultrasonic testing,Eddy current,detection,Leak detection,Galvanized