Good quality China Hot DIP Sch40 A53 API 5L Gr. B Seamless/Spiral Welded /ERW/Galvanized Carbon Steel Pipe

Overview

We'll make each individual effort to become exceptional and ideal, and speed up our steps for standing inside the rank of worldwide top-grade and high-tech enterprises for A53 Gr. B Seamless/Welded Carbon Steel Pipe, We welcome you to visit our factory and look forward to establishing friendly business relationships with customers at home and abroad in the near future. All of our products and solutions comply with international quality standards and are greatly appreciated in a variety of markets around the world. If you are interested in any of our products or would like to discuss a custom order, remember to feel free to contact us. We have been looking forward to forming successful business relationships with new clients in the near future.

ASTM A53 specifies the requirements for seamless/welded black and hot-dip galvanized steel pipes for general use. The steel listed in the standard must be processed in an open-air furnace, alkaline oxygen or electric furnace, and must have the following chemical requirements: carbon, manganese, phosphorus, sulfur, copper, nickel, chromium, molybdenum and vanadium. The pipeline should be seamless or welded. Tensile, bending and flattening tests should be carried out to ensure that it must meet the standard mechanical properties. Hydrostatic pressure test shall be carried out, and no leakage through the weld or pipe body. Non-destructive electrical tests should be carried out to ensure that the total volume of the pipeline must meet the standard. If it is deemed necessary to ensure that the pipeline meets the specified requirements, the buyer has the right to carry out any inspections and tests specified in this specification.
ASTM A 53 is suitable for pressure piping systems, pipes for pipelines and general purpose pipes at a temperature of 350 degrees. Among them, Gr.B steel grade is the most commonly used, with its tensile strength ≥ 415 (MPa) and yield strength ≥ 240 (MPa).

Application

It Is Mainly Used for force and pressure parts, and for general purpose steam, water, gas and air pipes.

Main Grade

GR.A, GR.B

Chemical Component

Grade

 Component %,≤
C Mn P S

    CuA

  NiA

CrA

MoA VA
S type(seamless pipe)
GR.A 0.25B 0.95 0.05 0.045

0.40

0.40

0.40

0.15 0.08
GR.B 0.30C 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08
E type(Resistance welded pipe)
GR.A 0.25B 0.95 0.05 0.045

0.40

0.40

0.40

0.15 0.08
GR.B 0.30C 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08
F type(Furnace Welded Pipe)
A 0.30B 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08

A The sum of these five elements must not be greater than 1.00%。

B For every 0.01% decrease in the maximum carbon content, the maximum manganese content is allowed to increase by 0.06%, but the maximum cannot exceed 1.35%.

C Each 0.01% decrease in the maximum carbon content will allow the maximum manganese content to increase by 0.06%, but the maximum must not exceed 1.65%.

Mechanical Property

item GR.A GR.B

tensile strength, ≥, psi [MPa]

Yield Strength, ≥, psi [MPa]

Gauge 2in.or 50mm elongation

48 000 [330]30 000 [205]A,B 60 000 [415]35 000 [240]A,B

A The minimum elongation of gauge length 2in. (50mm) shall be determined by the following formula:

e=625000(1940)A0.2/U0.9

e = the minimum elongation of the gauge 2in. (50mm), the percentage rounded to the nearest 0.5%;

A = Calculated according to the specified outer diameter of the nominal tube or the nominal width of the tensile sample and its specified wall thickness, and rounded to the nearest cross-sectional area of the tensile sample of 0.01 in.2 (1 mm2), and It is compared with 0.75in.2 (500mm2), whichever is smaller.

U = specified minimum tensile strength, psi (MPa).

B For various combinations of different sizes of tensile test specimens and prescribed minimum tensile strength, the required minimum elongation is shown in Table X4.1 or Table X4.2, according to its applicability.

Test Requirement

Tensile test, bending test, hydrostatic test, nondestructive electrical test of welds.

Supply Ability

Supply Ability: 2000 Tons Per Month Per Grade Of ASTM A53/A53M-2012 Steel Pipe

Packaging

In Bundles And In Strong Wooden Box

Delivery

7-14 days if in stock, 30-45 days to produce

Payment

30% depsoit, 70% L/C or B/L copy   or  100% L/C at sight

Product Detail

Boiler Tube


GB/T 8162-2008


ASTM A519-2006


BS EN10210-1-2006


ASTM A53/A53M-2012


GB9948-2006


GB6479-2013


GB/T 17396-2009


  • Good quality China Hot DIP Sch40 A53 API 5L Gr. B Seamless/Spiral Welded /ERW/Galvanized Carbon Steel Pipe Related Video: