About competitive selling prices, we believe that you will be searching far and wide for anything that can beat us. We will state with absolute certainty that for such excellent at such charges we are the lowest level around for Hot Rolled ASTM A106 Gr.B Carbon Steel Seamless Pipe, With a wide range, good quality, fair rates and great services, we are going to be your ideal business partner. We welcome new and outdated prospects from all walks of lifestyle to get in touch with us for future company associations and achieving mutual accomplishment! Since its foundation , the company keeps living up to the belief of "honest selling , best quality , people-orientation and benefits to customers. " We are doing everything to supply our customers with best services and best merchandise . We promise that we are going to be responsible all the way to the end once our services begin.
Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature
Grade of high-quality carbon structural steel: GR.A,GR.B,GR.C
| Composition, ％ | |||
| Grade A | Grade B | Grade C | |
| Carbon, max | 0.25A | 0.3B | 0.35B |
| Manganese | 0.27-0.93 | 0.29-1.06 | 0.29-1.06 |
| Phosphorus, max | 0.035 | 0.035 | 0.035 |
| Sulfur, max | 0.035 | 0.035 | 0.035 |
| Silicon, min | 0.10 | 0.10 | 0.10 |
| Chrome, maxC | 0.40 | 0.40 | 0.40 |
| Copper, maxC | 0.40 | 0.40 | 0.40 |
| Molybdenum, maxC | 0.15 | 0.15 | 0.15 |
| Nickel, maxC | 0.40 | 0.40 | 0.40 |
| Vanadium, maxC | 0.08 | 0.08 | 0.08 |
| A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%. | |||
| B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%. | |||
| C These five elements combined shall not exceed 1%. | |||
| Grade A | Grade B | Grade C | ||||||
| Tensile strength, min, psi(MPa) | 48 000(330) | 60 000(415) | 70 000(485) | |||||
| Yield strength, min, psi(MPa) | 30 000(205) | 35 000(240) | 40 000(275) | |||||
| Longitudinal | Transverse | Longitudinal | Transverse | Longitudinal | Transverse | |||
| Elongation in 2 in. (50 mm), min, % Basic minimum elongation transverse strip tests, and for all small sizes tested in full section |
35 | 25 | 30 | 16.5 | 30 | 16.5 | ||
| When standard round 2-in. (50-mm) gauge length test specimen is used | 28 | 20 | 22 | 12 | 20 | 12 | ||
| For longitudinal strip tests | A | A | A | |||||
| For transverse strip tests, a deduction for each 1/32-in. (0.8-mm) decrease in wall thickness below 5/16 in. (7.9 mm) from the basic minimum elongation of the following percentage shall be made | 1.25 | 1.00 | 1.00 | |||||
| A The minimum elongation in 2 in. (50 mm) shall be determined by the following equation: | ||||||||
| e=625000A 0.2 / U 0.9 | ||||||||
| for inch-pound units, and | ||||||||
| e=1940A 0.2 / U 0.9 | ||||||||
| for SI units, | ||||||||
| where: e = minimum elongation in 2 in. (50 mm), %, rounded to the nearest 0.5%, A = cross-sectional area of the tension test specimen, in.2 (mm2), based upon specified outside diameter or nominal specified outside diameter or nominal specimen width and specified wall thickness, rounded to the nearest 0.01 in.2 (1 mm2). (If the area thus calculated is equal to or greater than 0.75 in.2 (500 mm2), then the value 0.75 in.2 (500 mm2) shall be used.), and U = specified tensile strength, psi (MPa). |
||||||||
In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe.
Supply Ability: 1000 Tons Per Month Per Grade of ASTM SA-106 Steel Pipe
In Bundles And In Strong Wooden Box
7-14 days if in stock, 30-45 days to produce
30% depsoit, 70% L/C or B/L copy or 100% L/C at sight